Aluminum stainless steel clad plate is a clad material composed of aluminum alloy plate and stainless steel plate, and its structure is composed of aluminum alloy plate and stainless steel plate. Aluminum stainless steel clad plates have the advantages of light weight, corrosion resistance, high strength, high temperature resistance, wear resistance, fatigue resistance, and good self-lubrication performance, and are widely used in construction, aviation, transportation, electronics, medical and other fields.
Specifications of Aluminum Clad Stainless Steel Plate:
|
Specification |
Details |
|
Plate Type |
Aluminum-Clad Stainless Steel Plate |
|
Base Material |
Stainless Steel (e.g., 304, 316, 310, or other stainless steel grades) |
|
Cladding Material |
Aluminum (Pure Aluminum or Aluminum Alloys, e.g., 1050, 1100) |
|
Clad Layer Thickness |
Typically 0.5 mm to 3 mm |
|
Base Stainless Steel Thickness |
Typically 5 mm to 50 mm |
|
Clad Ratio |
Clad thickness to base material thickness ratio: ~1:5 to 1:20 |
|
Bonding Method |
Roll bonding, Explosive bonding, Diffusion bonding, Hot rolling |
|
Hardness of Stainless Steel Base |
Rockwell B 70 to 95 (depends on grade of stainless steel used) |
|
Hardness of Aluminum Cladding |
Vickers hardness 15-50 (depending on aluminum alloy used) |
|
Tensile Strength (Stainless Steel Base) |
500 - 850 MPa (depends on grade of stainless steel) |
|
Tensile Strength (Aluminum Cladding) |
90 - 250 MPa (depending on aluminum alloy used) |
|
Corrosion Resistance |
Stainless steel provides excellent corrosion resistance, while aluminum offers good resistance to atmospheric corrosion |
|
Thermal Conductivity |
Stainless Steel: 15-20 W/m·K, Aluminum: 205-235 W/m·K |
|
Electrical Conductivity |
Aluminum: 60-65% IACS (International Annealed Copper Standard) |
|
Density |
Stainless Steel: ~7.85 g/cm³, Aluminum: ~2.70 g/cm³ |
|
Maximum Service Temperature |
Stainless Steel: ~870°C (depending on grade), Aluminum: ~200°C |
|
Applications |
Chemical processing, heat exchangers, storage tanks, marine applications, electrical components, aerospace, and automotive |
|
Weldability |
Good, but requires careful control to avoid interface issues; often TIG welding or other special techniques are used |
|
Surface Finish |
Available in various finishes, such as 2B, No. 1, or polished finishes on the stainless steel side |
|
Industry Standards |
ASTM B899 (for aluminum-clad materials), ASME BPVC Section II for pressure vessel applications |
The main features of aluminum stainless steel clad plates are as follows:
Light weight: The weight of the aluminum stainless steel clad plate is only about 1/3 of the traditional pure aluminum panel, which can greatly reduce the load of the building and reduce the cost of the structure.
Corrosion resistance: The surface of the aluminum stainless steel clad plate has good corrosion resistance, which can effectively prevent the erosion of buildings by corrosive gases such as acid rain and salt spray.
High strength: Aluminum stainless steel clad plates have very high strength and can be made into various structural parts or parts with complex shapes, uneven thickness and heavy loads.
High temperature resistance: Aluminum stainless steel clad plates can withstand high temperatures up to 1000°C, so they are very useful in many high temperature applications.
Wear resistance: The wear resistance of aluminum stainless steel clad plates is very good, which can effectively reduce friction, reduce wear and tear, and prolong the service life of buildings.
Conductivity: Aluminum conducts electricity even better than copper.
Application of Aluminum-clad steel explosion composite plate :
Architectural decoration works: The aluminum-clad steel explosion composite plate has the characteristics of being lightweight and high strength, easy to process, beautiful and generous, can be made into a variety of decorative lines, sculptures, railings, etc., and is widely used in architectural decoration projects.
Radiator manufacturing: due to the aluminum-clad steel explosion composite plate having good thermal conductivity and corrosion resistance, it can be used to manufacture automobiles, electronic equipment, and other occasions of radiators to improve the reliability and service life of the equipment.
Pipeline manufacturing: Aluminum-clad steel explosion composite plate has good corrosion resistance and processing performance and can be used to manufacture water pipes, gas pipes, oil pipelines, and other pipeline equipment.
Mechanical parts manufacturing: aluminum clad steel explosion composite plate has excellent plasticity and flexibility and can manufacture various mechanical parts, such as gears, bushings, screws, and so on. At the same time, its strength and corrosion resistance also make it in the manufacture of mechanical parts has a wide range of application prospects.
Medical device manufacturing: Due to its good thermal conductivity and corrosion resistance, aluminum-clad steel explosion composite plates can manufacture medical devices, such as surgical instruments, implants, and so on. At the same time, its lightweight and high strength characteristics also make the application in the medical field have advantages.