1. Good shape, high tolerance, versatility and blemish-free surfaces.
2. Used in commercial and general engineering applications such as bus bodies, cladding and fan blades.
3. The demands of its ever-growing clientele with continuous upgrades and process improvement.
4. MOQ 2MT
Dimensions |
Parameter |
Range |
Standard |
Tolerance |
Thickness (mm) |
0.16 _ 5.00 |
|
for 0.16 to 0.29 +/-0.01 |
for 0.30 to 0.71 +/-0.05 |
for 0.72 to 1.40 +/-0.08 |
for 1.41 to 2.00 +/-0.11 |
for 2.01 to 4.00 +/-0.12 |
Width (mm) |
50 _ 1620 |
1219, 1500 |
Slit coil: +2, -0 |
I.D (mm) |
75,150,305,405,505 |
|
|
Coil density (kg/mm) |
6 max |
|
|
Stucco embossed coils are also available in the thickness range of 0.30 _ 1.10 mm. |
Alloy (AA) |
Temper |
UTS (mpa) |
%E (min)
(50mm gauge length)
|
Min |
Max |
0.50 _ 0.80 mm |
0.80 _ 1.30 mm |
1.30 _ 2.6 0mm |
2.60 _ 4.00 mm |
1050 |
O |
55 |
95 |
22 |
25 |
29 |
30 |
1050 |
H14 |
95 |
125 |
4 |
5 |
6 |
6 |
1050 |
H18 |
125 |
- |
3 |
3 |
4 |
4 |
1070 |
O |
- |
95 |
27 |
27 |
29 |
34 |
1070 |
H14 |
95 |
120 |
4 |
5 |
6 |
7 |
1070 |
H18 |
120 |
- |
3 |
3 |
4 |
4 |
1200, 1100 |
O |
70 |
110 |
20 |
25 |
29 |
30 |
1200, 1100 |
H14 |
105 |
140 |
3 |
4 |
5 |
5 |
1200, 1100 |
H16 |
125 |
150 |
2 |
3 |
4 |
4 |
1200, 1100 |
H18 |
140 |
- |
2 |
2 |
3 |
3 |
3103, 3003 |
O |
90 |
130 |
20 |
23 |
24 |
24 |
3103, 3003 |
H14 |
130 |
180 |
3 |
4 |
5 |
5 |
3103, 3003 |
H16 |
150 |
195 |
2 |
3 |
4 |
4 |
3103, 3003 |
H18 |
170 |
- |
2 |
2 |
3 |
3 |
3105 |
O |
95 |
145 |
14 |
14 |
15 |
16 |
3105 |
H14 |
150 |
200 |
4 |
4 |
5 |
5 |
3105 |
H16 |
175 |
215 |
2 |
2 |
3 |
4 |
3105 |
H18 |
195 |
- |
1 |
1 |
1 |
2 |
8011 |
O |
85 |
120 |
20 |
23 |
25 |
30 |
8011 |
H14 |
125 |
160 |
3 |
4 |
5 |
5 |
8011 |
H16 |
150 |
180 |
2 |
3 |
4 |
4 |
8011 |
H18 |
175 |
- |
2 |
2 |
3 |
3 |
Chemical composition |
Alloy (%) |
AA 1050 |
AA 1200 |
AA 3003 |
AA 3103 |
AA 3105 |
AA 8011 |
Fe |
0.40 |
1.00 |
0.70 |
0.70 |
0.70 |
0.60 _ 1.00 |
Si |
0.25 |
(Fe + Si) |
0.60 |
0.50 |
0.6 |
0.50 _ 0.90 |
Mg |
- |
- |
- |
0.30 |
0.20 _ 0.80 |
0.05 |
Mn |
0.05 |
0.05 |
1.0 _ 1.50 |
0.9 _ 1.50 |
0.30 _ 0.80 |
0.20 |
Cu |
0.05 |
0.05 |
0.05 _ 0.20 |
0.10 |
0.30 |
0.10 |
Zn |
0.05 |
0.10 |
0.10 |
0.20 |
0.25 |
0.20 |
Ti |
0.03 |
0.05 |
0.1 (Ti + Zr) |
0.1 (Ti + Zr) |
0.10 |
0.08 |
Cr |
- |
- |
- |
0.10 |
0.10 |
0.05 |
Each (others) |
0.03 |
0.05 |
0.05 |
0.05 |
0.05 |
0.05 |
Total (others) |
- |
0.125 |
0.15 |
0.15 |
0.15 |
0.15 |
Al |
99.50 |
99 |
Remainder |
Remainder |
Remainder |
Remainder |
Single number indicates maximum content |
Parameter |
Range |
Tolerance |
Thickness (mm) |
0.3 _ 2.00 |
for 0.30 to 0.71 +/-0.05 |
for 0.72 to 1.4 +/-0.08 |
for 1.41 to 2.00 +/-0.11 |
Width (mm) |
50 _ 1250 |
Slit coil: +2, -0 |
I.D (mm) |
203, 305, 406 for thickness < 0.71 |
- |
406, 508 for thickness > 0.71 |
Density (kg/mm) |
3.5 max |
- |
Mechanical properties |
Alloy (AA) |
Temper |
UTS (mpa) |
%E (min)
(50mm gauge length) |
Min |
Max |
3004 |
O |
150 |
200 |
10 |
3004 |
H32 |
193 |
240 |
1 |
3004 |
H34 |
220 |
260 |
1 |
3004 |
H36 |
240 |
280 |
1 |
3004 |
H38 |
260 |
- |
1 |
5005 |
O |
103 |
144 |
12 |
5005 |
H32 |
117 |
158 |
3 |
5005 |
H34 |
137 |
180 |
2 |
5005 |
H36 |
158 |
200 |
1 |
5005 |
H38 |
180 |
- |
1 |
5052 |
O |
170 |
210 |
14 |
5052 |
H32 |
210 |
260 |
4 |
5052 |
H34 |
230 |
280 |
3 |
5052 |
H36 |
255 |
300 |
2 |
5052 |
H38 |
268 |
- |
2 |
5251 |
O |
160 |
200 |
13 |
5251 |
H32 |
190 |
230 |
3 |
5251 |
H34 |
210 |
250 |
3 |
5251 |
H36 |
230 |
270 |
3 |
5251 |
H38 |
255 |
- |
2 |
Alloy (%) |
AA 3004 |
AA 5005 |
AA 5052 |
AA 5251 |
Fe |
0.70 |
0.70 |
0.40 |
0.50 |
Si |
0.30 |
0.30 |
0.25 |
0.40 |
Mg |
0.80 _ 1.30 |
0.50 _ 1.10 |
2.20 _ 2.80 |
1.80 _ 2.40 |
Mn |
1.00 _ 1.50 |
0.20 |
0.10 |
0.10 _ 0.50 |
Cu |
0.25 |
0.20 |
0.10 |
0.15 |
Zn |
0.25 |
0.25 |
0.10 |
0.15 |
Ti |
- |
- |
- |
0.15 |
Cr |
- |
0.10 |
0.15 _ 0.35 |
0.15 |
Each (others) |
0.05 |
0.05 |
0.05 |
0.05 |
Total (others) |
0.15 |
0.15 |
0.15 |
0.15 |
Al |
Remainder |
Remainder |
Remainder |
Remainder |
Single number indicates maximum content |